PolyPadsuper-chock PP11, Epoxy Systems
Compounds and Composites
Epoxy Systems
PolyPadsuper-chock PP11
Product Description
Epoxy Chocking Resin.
Product Ratings
Heat deflection temperature 87 Deg. C, GB/T 1634.1-2004; | Barcol hardness 60, GB/T 3854-2005; | Linear shrinkage 0.016%, ASTM D2566-86; | Tensile strength 41.4MPa, ASTM D638-2010; | Tensile Modulus 8534MPa, ASTM D638-2014; | Compressive Strength 133.4MPa, GB/T 1041-2008; | Compression Modulus 5596MPa, GB/T 1041-2008; | Specific gravity 1.69 g/cm3, GB/T 1033.1-2008; . | Water absorption 0.06%(24h),0.22%(48h), ISO175-2010; | Oil absorption(diesel) 0.06%(24h),0.21%(48h), ISO175-2010; | Oil absorption(lubricant) 0.1%(24h),0.45%(48h), ISO175-2010; | Fire resistance HB, GB/T 2408-2008 | | The maximum static surface pressure at service temperature is as follows: | 10.0 N/mm2 at 20 Degree C | 9.4 N/mm2 at 30 Degree C | 8.7 N/mm2 at 40 Degree C | 8.0 N/mm2 at 50 Degree C | 7.0 N/mm2 at 60 Degree C | 5.9 N/mm2 at 70 Degree C | 4.5 N/mm2 at 80 Degree C | 2.2 N/mm2 at 90 Degree C
Applicable Standards
ISO 175-2010
GB/T 3854-2005, GB/T 1041-2008, GB/T 1033.1-2008, ASTM D638-2014, ASTM D256-2010, ASTM D2566-1986
CB/T 3514-2015