Metal polymer DIAMANT MM1018P and DIAMANT MM1018FL
Compounds and Composites
Composite Materials
Metal polymer DIAMANT MM1018P and DIAMANT MM1018FL
Product Description
Metal polymer MM1018 is a filler containing 2-component reaction resin system (epoxy resin) in pasty, "MM1018P" No.1436, or liquid, "MM1018FL" No.1866, consistency., For the product MM1018P Paste, the mixed MM1018 is applied to the contact surface in an X-shape. Further information on the material and processing can be taken from the technical datasheet "TD-MM1018-P-1436_EN"., For the product MM1018FL Liquid, the application can take place through casting or injecting. Information on the material and processing can be taken from the technical datasheet "TD-MM1018-FL-1866_EN".
Product Ratings
For MM1018 Paste No.1436: | Density: 2.4 g/cm | E-module: 10,000 N/mm | Shore hardness: 89 | Compressive strength: 110 N/mm | Shrinkage: 0.84 mm/m | Viscosity: 600 Pas | Pot life (T15K): 20 minutes | Creep coefficient (DIN EN ISO 13584:2003-11): 2.1 | Thermal expansion coefficient (-20 to +60 C): 2.5E-05 1/K | Temperature resistance: -40 to +90C | Mixing ratio by weight: A = 3.7 : B = 1 | - For MM1018 Liquid No.1866: | Density: 2.4 g/cm | E-module: 10,000 N/mm | Shore hardness: 88 | Compressive strength: 161 N/mm | Shrinkage: 0.35 mm/m | Viscosity: 11000 mPas | Pot life (T15K): 89 minutes | Creep coefficient (DIN EN ISO 13584:2003-11): 1.1 | Thermal expansion coefficient (-20 to +60 C): 2.89E-05 1/K | Temperature resistance: -40 to +90C | Mixing ratio by weight: A = 21.4 : B = 1
Applicable Standards
DIN EN13412:2006
DIN EN 12190:1998-12
DIN EN 12617-4:2002
DIN EN 12614: 2005-01
DIN EN ISO 3219:1994
DIN EN ISO 13584:2003-11
DIN EN ISO 9514:2005-07
DIN EN ISO 868:2003-10